MCI-2000钢筋阻锈剂对于桥梁甲板的防腐蚀应用
Minnesota D.O.T. Study Project
LOCATION
Randolph St. Over I-35 in St. Paul, MN
PRODUCT
MCI-2000
HISTORY
The Randolph St. bridge deck was rehabilitated in 1986. This included milling the deck to a depth of
0.5 inches (13mm) and removing areas of unsound concrete. A patch and overlay with low
slump dense concrete (LSDC) was applied. The eastbound lane was used as control, while the west bound lane was treated with MCI-2000 admixture at 1 pint per cubic yard (0.6 liter per cubic
meter).
The year 2000 update showed neither side has entered active corrosion. However, the MCI®
treated side still has lower corrosion potentials and corrosion rates than the control side. Chloride
analysis showed the MCI® treated side should not initiate corrosion until the year 2022, while the
control side should begin corroding in the year 2005 (17 year increase in service life).
Gas Chromatography analysis showed the presense of MCI-2000 at a 3” depth after 15 years, on the treated side, while no MCI-2000 was on the control side (as expected).
深圳市丰安科技有限公司是美国CORTEC公司中国总代理，15年来提供原装进口 VPCI 377、VPCI 146、VPCI 369、VPCI 126、VPCI 329 、VPCI649等气相防锈材料，百家上市企业指定供应商。咨询热线：0755-25549278 / 13380394278
“推荐阅读”
Cortec防锈推荐
相关技术资讯
- 铸件防锈使用哪种防锈剂性价比最高？
- 山东某数控机械配件防锈使用VPCI-369CORTEC防锈油
- 某科技公司电子线路防锈使用VPCI-132/VPCI-111
- VpCI-111 Emitter
- VpCI-609 Corrosion Inhibiting Powder for Ferrous Metals
- VpCI-337 Waterborne Corrosion Inhibitor
- VpCI-369D Oil Based Temporary Coating
- VpCI-309 Powders
- 如何通过一个简单的步骤保护电气和电子产品免受腐蚀
- 新车辆传感器的腐蚀保护帮手VPCI-146防锈纸